Cyanolit® 201 is a very low-viscosity, fast-curing adhesive with excellent capillary action. Particularly suitable for small-area bonds and for applications where the adhesive can only be applied after the basic assembly, due to production or construction.
Curing takes place without heat supply, pressure or additional activators. The classical one-component cyanoacrylates react with moisture, which is absorbed as a moisture film on the material surfaces, in a few seconds.
The curing speed depends on the gap width and the humidity level. A small gap width and a high humidity accelerate the setting process.
After a short time Cyanolit® reaches high strength. The material continues to harden 24 hours after gluing. Only after this time is the optimum media resistance achieved.
Temperature resistance: -80 to +80 °C (cured)
Viscosity: 1 - 3 mPas (Brookfield LVT, 25 °C, Sp 2/ 60rpm) (non-cured)
Flash point: > +83 °C (PE-Norm 050, non-cured)
Curing time / Tensile strength:
PVC hard: 7 sec. / 5.5 MPa
ABS: 12 sec. / 5.4 MPa
PA 6.6: 20 sec. / 4.3 MPa
PVC/Stahl: 15 sec. / 7.0 MPa
AI/ABS: 15 sec. / 5.0 MPa
Neopren PVC: 5 sec. / 0.5 MPa
Neopren / ABS: 20 sec. / 0.5 MPa
Storage: 6 months at +20 °C, max. 9 months at 0 to +10 °C