window.ga=window.ga||function(){(ga.q=ga.q||[]).push(arguments)};ga.l=+new Date; ga('create', 'UA-32196581-2', 'auto'); ga('set', 'forceSSL', true); ga('set', 'anonymizeIp', true); ga('require', 'displayfeatures'); ga('require', 'cleanUrlTracker'); ga('require', 'outboundLinkTracker'); ga('require', 'ec'); ga('send', 'pageview'); ga('set', 'nonInteraction', true); setTimeout("ga('send', 'event', 'read', '20 seconds')", 20000); Glass Ceramic Test Package | Reichelt Chemietechnik
+49 (0) 6221-3125-0 (Mon-Wed 8 am - 17 pm, Thu-Fri 8 am - 16 pm)

Glass Ceramic Test Package

Product specification Content: 1 round rod 10 x 50 mm; 1 block 10 x 10 x 25 mm; 1... more

Product specification

Content: 1 round rod 10 x 50 mm; 1 block 10 x 10 x 25 mm; 1 plate 3 x 25 x 50 mm.

General Information Highest temperature ceramic Absolute chemical resistance No uptake of... more

General Information

Highest temperature ceramic

Absolute chemical resistance

No uptake of humidity

Non-porous

Not deformable

Great hardness

Outstanding insulating material at high voltages, a high frequency range at high temperatures

Achievable manufacturing tolerances up to 0.013 mm

Achievable surface roughness >0.5 µm to 0.013 µm (polished)

Processing can be done with usual metal processing tools for metal (metal cutting), thus purchase of expensive diamond tools is not necessary.

Material: glass ceramic

Colour: white

Temperature range: -200 to +800 °C, for a short time +1,000 °C

Special features: highest temperature loadability, great hardness, achievable manufacturing tolerances up to 0.013 mm

Expansion coefficient:

at -200 to +25 °C: 74 x 10-7 / °C;

at +25 to +800 °C: 126 x 10-7 / °C

Specific heat (+25 °C): 0.79 kJ/kg x K

Heat conduction (+25 °C): 1.46 W/m * °C

Heat diffusion (+25 °C): 7.3 x 10-7 m2/s

Density: 2.52 g/cm3

Porosity: 0 %

Elastic modulus: 66.9 GPa (Youngs modulus)

Shear modulus: 25.5 GPa

Rockwell hardness: M 48

Tensile strength: 94 MPa (modulus of rupture)

Pressure resistance: 345 MPa

Breaking strength: 1.53 MPa M 0.5

Dielectric constant: 6.03 at 1 kHz; 5.67 at 8.5 GHz

Dielectric strength (GS/WS): 40 kV/mm at 0.01 thickness, +25 °C

GS-Volume resistivity: >1016 Ohm/cm