Molecular sieve 10 Å (1.0 nm).
Removal of water and carbon dioxide out of air, nitrogen, oxygen and other inert gases. During the process a dew point of -75 °C and a carbon dioxide portion of <1 ppm are reached. Simultaneously elimination of hydrogen sulfide and mercaptans (natural gas purification) takes place.
Adsorbs H2O, CO2, H2S, NH3, CO and others
Material: 13 X molecular sieve; sodium aluminosilicate (sodalite basic structure)
Shape: beads, Ø 1.6 to 2.5 mm
Dew point: <-75 °C
Water uptake capacity: 29 % by weight at +20 °C, 20 to 100 % rel. air humidity
General Information Granular Material
Separation of solid or liquid particles out of gases.
Production of pure and purest reference and analysis gases by mechanical separation (filtration) as well as physical and chemical separation (adsorption and catalysis).
Fine gas purification is performed by catalysis and adsorption allowing reduction of contaminants up to few ppb.
General Information Sorbent
Unlimitedly regenerable sorbent material with very high dimensional stability and abrasion resistance for fine purification of gases and fluids.
Exactly classified sorbent with crystal lattice structure.
Molecular sieves ensure complete drying of gases.
Selective adsorption of hydrocarbons.
Very high dimensional stability and abrasion resistance.
Unlimitedly repeatable regeneration without impact on efficiency. Activation at +300 to +350 °C in the dry inert gas flow.
Predrying of the gases with commonly used desiccants is recommended to avoid excessive exhaustion of the molecular sieve. Molecular sieves are finally used for fine drying.
Extremely high adsorptive effect during gas drying even at highest flow speed (5-15 m/min).
Adsorption rate in the fluid phase is smaller by factor 10 compared to the gas phase, therefore flow speed is lower (0.5-1.5 m/min).
4 Å: synthetic and crystalline zeolite (A-type); sodium aluminosilicate
10 Å: 13 X molecular sieve; sodium aluminosilicate (sodalite basic structure)
Bulk volume: approx. 600 to 700 g/l
Loss by drying: <2 % at +300 °C
Regeneration temperature: at +300 °C to +350 °C in dry inert gas flow
Temperature range: 0 to +100 °C
Functional cookies are absolutely necessary for the functionality of the webshop. These cookies assign a unique random ID to your browser to ensure your uninterrupted shopping experience across multiple page views.
Marketing Cookies dienen dazu Werbeanzeigen auf der Webseite zielgerichtet und individuell über mehrere Seitenaufrufe und Browsersitzungen zu schalten.
Tracking cookies help the shop operator to collect and evaluate information about the behaviour of users on their website.