High-Chem Welding Wire made of MFA

High-Chem Welding Wire made of MFA
High-Chem Welding Wire made of MFA
 
   
Product specification MFA is a newly developed fluorinated plastic, highly resistant and... more

Product specification

MFA is a newly developed fluorinated plastic, highly resistant and suitable for extreme mechanical and thermal loads

Lowest embrittlement at temperature load

High resistance to weathering

Very good mechanical stability from lowest temperatures up to +250 °C

Volume resistivity, dielectric constant and loss factor independently of the temperature

Outstanding thermal stability (weight loss <0.3 % at +380 °C, 50 min. in air)

Non-oxidizing

Technical specification

Material: MFA (modified fluoralkoxy)

Colour: natural

Density: 2.12 - 2.17 g/cm3

Temperature range: -70 to +240 °C

Melting point: +290 °C

Embrittlement temperature: -80 °C

Coefficient of sliding friction against steel (dry): 0.1 - 0.2

Tearing strength: 28 - 36 N/mm2 at +23 °C; 15 - 21 N/mm2 at +150 °C; 6 - 8 N/mm2 at +250 °C

Shore hardness D: 59° (DIN 53505)

Buckling strength 0.3 mm (cycles): 70,000 - 100,000

Coefficient of thermal expansion: at +23 to +150 °C (1/K) 12 - 20 x 10-5

Water absorption: <0.03 %

Oxygen index: >95 %

Flammability rating: UL 94 V-0

Dielectric constant: 2.0 at 50 Hz

Volume resistivity: >1016 Ohm x cm

Surface resistivity: >1017 Ohm/cm2

Dielectric strength: 34 - 38 kV (thickness 1 mm)

No additional information available.