L-Profile made of Glass Fiber Reinforced Plastic GFRP

No additional information available.
General Information Use in laboratory technology, electroplating technology and electrical... more

General Information

Use in laboratory technology, electroplating technology and electrical engineering.

Linear stress-strain behavior

Low weight

Electrically insulating

Chemical-resistant

Corrosion-resistant and weatherproof

UV-resistant

Halogen-free

High economic efficiency

High stability

Metal-free, unmagnetic

Thermally insulating

The unsaturated polyester resins are among the most commonly used resins in composite materials. UP resins are a colourless to slightly yellow solution of unsaturated polyester in a reactive solvent, usually styrene. At room temperature or by supply of heat, they are cured, whereby a heat reaction is released.

Material:

Resin: polyester

Reinforcing fibers: glass fibers

Design: pultruded

Color: dark gray / white

Density: 2 g/cm3

Temperature range: -100 to +155 °C, for a short time +180 °C

Impact toughness (IZOD): 300 kJ/m2

Interlaminar shear strength: 25 MPa

Volume resistivity: 1010 - 1015 Ohm * cm

Surface resistance: 1010 - 1015 Ohm

Breakdown strength: 5 - 10 kV/mm

Comparative tracking index (CTI): KA 3c / KB 500 / KC 600

Dielectric constant: <5

Coefficient of linear thermal expansion: 12 x 10-6 1/K

Thermal conductivity: 0.2 - 0.6 W/m*K

Specific heat capacity: 1.0 - 1.2 kJ/kg*K

Water absorption: 0.15 %

Dimensional stability by Martens method: +200 °C

Resistance to glow heat: level 2b

Elongation at break: 1.0 - 1.8 %

Barcol hardness: >40

Tolerances:

Height and width: ±0.5 %

Wall thickness: 0 - 2 mm ±0.15 mm, 2 - 5 mm ±0.20 mm, 5 - 10 mm ±0.35 mm

Flammability rating: B2, UL 94 V-1, ASTM D635

Burning behaviour: Self-extinguishing

All following measured values are depending on the test direction: parallel (II) or perpendicular (+) to the fibers.

Tensile strength: II: 250 MPa; +: 30-80 MPa

Tension stress: II: 135 MPa (short-term); 70 MPa (long-term)
+: 20 MPa (short-term); 15 MPa (long-term)

Bending strength: II: 250 MPa; +: 30-80 MPa

Bending stress: II: 135 MPa (short-term); 70 MPa (long-term)
+: 20 MPa (short-term); 15 MPa (long-term)

Elastic modulus tensile strength: II: 23.000 MPa; +: 8.000 MPa

Elastic modulus bending: II: 25.000 MPa; +: 9.000 MPa

Compressive strength: II: 450 MPa; +: 90 MPa

Compressive stress: II: 135 MPa (short-term); 70 MPa (long-term)
+: 25 MPa (short-term); 20 MPa (long-term)

Compressive modulus: II: 1.000 MPa; +: 4.000 MPa

Item Image A
mm
B
mm
C
mm
Length
mm
Einheit
Stück
Price
Euro*
Buy
306420
20 20 3 500 1 43.00
306421
20 20 3 1.000 1 73.00
306422
30 30 5 500 1 54.00
306423
30 30 5 1.000 1 90.00
306424
40 40 3 500 1 78.00
306425
40 40 3 1.000 1 129.00
306426
40 40 5 500 1 95.00
306427
40 40 5 1.000 1 159.00
306428
40 40 8 500 1 101.00
306429
40 40 8 1.000 1 180.00